Flux cored wire of software - AH106/software - NP - 10X14T/
Flux cored wire of the software brand - AH106 is intended for automatic and semi-automatic building up of the parts working in the conditions of friction of metal about metal in the corrosion environment. It is recommended for building up on a direct current of the return polarity. The wire is issued with a diameter of 1,6 - 3,0mm.
Svarochno - technology properties
Forming of the deposited bead - good
Separability of a slag crust - good
Coefficient of building up, g/Ah - 12 - 16
Tendency of the built-up metal
to flawing - small
Wire expense on 1 kg
the built-up metal, kg - 1,15 - 1.25
Hardness of the built-up metal
after building up of HRC42 - 48
after issue of HRC 28 - 32
The recommended building up modes
|Diameter of a wire, mm||
|Speed of building up, m/h|
|1,6 - 1,8||160 - 250||23 - 26||15 - 20|
|2,0 - 2,2||200 - 300||24 - 27||15 - 20|
|2,4 - 2,6||240 - 360||24 - 27||20 - 25|
|2,8 - 3,0||280 - 400||26 - 29||20 - 25|
Properties of the built-up metal
Well resists corrosion and wear at friction of metal about metal in the environment of steam with a pressure of 400 kgfs/cm ² and temperature to 450ºС. Processing by cutting without the softening heat treatment is possible.
Building up is in most cases made without preheating. At building up of massive parts it is necessary preliminary podogrevdo 250 - 350ºС. Heat treatment: issue at a temperature of 560 - 580ºС during 2 h or annealing at 860 - 870ºС, endurance of 2 h, with the subsequent tempering. Perhaps, also execution of a wire for building up under gumboils of brands: AH-20C, AH-20P, AH-26C, AH-26P, and also in protective gases (CO2, Ar + CO2 and pure argon).
Building up of plungers, sealing surfaces of common industrial, gas and oil armature, rods gidrokrepy, etc.