- Country of manufactureBelarus
- Type of useUniversal
- Type of primerCorrosion
- Processed materialConcrete
- Colorless materialYes
Type: a one - component primer enamel is a suspension of
anticorrosive pigments and fillers in a modified alkyd varnish with the addition of functional additives desiccant and solvent. It does not contain lead and chromium.
Scope: primer enamel is intended for painting bridges, axles and other chassis parts at the line color bridge and axes in RC ZAA, nevidovyh parts automotive equipment chassis on the line coloration detail exhaust and chassis system RTMC PKZ, parts and components of automobile and bus art color - line shop
platforms and welded assemblies of "MAZ".
- a tailor formula high - binder additives and ground enamel has a high protective and decorative properties;
- priming enamel has excellent adhesion to metal and when applied in a single layer may be used as a primer;
- two - layer coating primer enamel coating replaces the complex consisting of several layers of primer and enamel.
- primer enamel is resistant to changes in temperature from - 60 ° C to plus 100 ° C;
- priming enamel does not contain lead and chromium.
The aforementioned advantages simplify the process as much as possible staining of metal surfaces.
Surface preparation: surface preparation products for painting primer enamel is carried out in accordance with the requirements of technical regulations on the product or GOST 9.402.
The metal surface before applying the primer enamel must be thoroughly cleaned of rust, scale and other debris, tipped, freed of dust, degreased and thoroughly dried. To eliminate condensation substrate temperature should be above the dew point temperature at least 3 ° C.
Coating: primer enamel is applied by air spraying, electrostatic spraying, or in small portions, the brush (in the case of defective places tinting). When applied by pneumatic spraying primer enamel is diluted with solvents: xylene (GOST 9410), o - xylene (TU BY 300042199.015), Oil solvent (GOST 10214) in an amount of not more than 30% by weight of a ground enamel. When spraying in Elektropol primer enamel is diluted with solvent to oil (GOST 10214) in an amount of not more than 30% by weight of a ground enamel.
Primer enamel is applied to the prepared surface at 15 - 35 ° C and relative humidity of 80% . Drying time two - layer coating thickness of 40 - 60 microns at a temperature (80 ± 2) ° C not more than 35 m, a thickness of 50 - 70 microns at a temperature of (100 ± 2) ° C not more than 30 minutes. Recommended operating viscosity primer enamel is 20 - 25 on - type viscometer VZ - 246 with a nozzle diameter of 4 mm at a temperature of (20,0 ± 0,5) ° C. The user independently makes the selection of a viscosity depending on the operating conditions (the ambient temperature in the room, the spray gun nozzle diameter,
working air pressure and others. ).
Exposure coating before using - not less than 5 days. Available subassembly components without damaging the coating 1 hour after drying.
Consumption Consumption primer enamel in a two - layer dry coating thickness of 40 - 60 microns is 120 - 180 g / m2, thickness of 50 - 70 microns - 150 - 210 g / m2, excluding the complexity of the painted surface, surface preparation, application method, soil - color enamel, staff development and other factors.
Precautions: during painting work in confined spaces, as well as after their completion requires careful ventilation. For hands protecting use rubber gloves.
Storage: priming enamel stored in a tightly closed container, protected from moisture and direct sunlight. Keep away from fire. In the case of storage at low temperatures priming before application of the enamel incubated in a warm room for at least 24 hours.
Warranty period: 12 months from date of manufacture.