RuBond ES180 B (50ml) One-component epoxy adhesive composition, thermoset buy in Lipetsk
ALL.BIZ Russia Russia products Chemical industries Adhesives & sealants Glues Epoxy adhesive RuBond ES180 B (50ml) One-component epoxy adhesive composition, thermoset
Buy RuBond ES180 B (50ml) One-component epoxy adhesive composition, thermoset
RuBond ES180 B (50ml) One-component epoxy adhesive composition, thermoset
rubond_es180_b_2000ml_odnokomponentnaya
rubond_es180_b_2000ml_odnokomponentnaya
rubond_es180_b_2000ml_odnokomponentnaya

RuBond ES180 B (50ml) One-component epoxy adhesive composition, thermoset

In stock
Price:
3468 RUB
Wholesale:
  • 1834 RUB/pcs  - from 100 pcs
Payment:
  • Invoice payment,
  • Cash,
  • T/T - Telegraphic Transfer,
  • Visa/Mastercard
  • In detail
Shipping:
  • Customer pickup,
  • Courier,
  • Transport company
  • In detail
Seller
Russia, Lipetsk
(View map)
+7(8 
Display phones

Company rating

100% of positive reviews from 5
1
1 year on Allbiz
Quickly responds
Technical characteristics
  • BrandRuBond
  • Country of manufactureRussia
  • ColorЧерный, однородный
Description

RuBond ES1 8 0 B is a one - component  epoxy adhesive composition .     

This composition is used for forming durable thermally conductive adhesive bonding , comparable in strength with welding,  and allows the system to replace traditional fastening parts , especially soldered  and welded, and  b oltovoe, Klep full - time , clamp ovoe .   

This adhesive has excellent adhesion to various materials: metals, ceramics, ferrite, glass, composites , concrete, artificial stone, almost all plastic and,  and etc. , and is used for gluing them in various combinations .    

Glue is optimal for use where necessary to form a thermally conductive interfacing parts and high demands on the strength characteristics of the adhesive compound, with simultaneous resistance spreadable when heated at a polymerization time , exclusion of d tekov adhesive .  

The adhesive is suitable for joints with large gaps between the mating parts (up to 5 mm).  

To Leu is about dnokomponentn th  Epoxy second  composition it , pre elapsed s  process of degassing  and ready oh  for use.  

 In contrast , and  by two - component adhesives, n Allows eliminate the difficulties of working with two - component adhesive compositions, their need to weigh  and mix prior to use.  

Eliminates the inevitable traditional loss of material residues  in the shipping and working containers, on working tools.  

The composition allows minimization th e  waste 's  production and optimize the shelf life of the finished adhesive to the stock , and reduce costs .  

   

 

Areas of  application:  

  • Aerospace 

  • Electronics 

  • Petrochemical industry 

  • Automotive industry 

  • Shipbuilding 

  • Optics production 

  • N riborostroeni e 

  • Manufacturing of composites 

  • Manufacture electron t ropriborov and appliances 

  • Telecommunication  activities 

  • Defense activities 

 

Application examples:  

 

  • Bonding of ferrites in electric motors , speakers , annunciators s microphone ah  , etc.  

  • Connection and filling of Sm - Co (rare earth) magnets in generators, magnetic lenses and couplings, magnetic flaw detectors  

  • SIC  (silicon carbide) connection with various materials: arrays in mirror elements , in various optical systems of telescopes and lasers 

  • Connecting laser packages in optical systems 

  • C to replenie  elements microsensor  

  • Assembly of mounting grids in telescopes (titanium alloy, silicon, invar) 

  • Bonding metal parts with various composites in automotive, aircraft, mechanical engineering, etc.  

  • Fastening mirrors to various surfaces 

  • Connection with simultaneous insulation of metal parts with different electronic potentials ( heatsink assembly made of copper and aluminum) 

  • Bonding and sealing  solar panels (solar panel and aluminum) 

  • Restoration of bearing seats, "pasting" of damaged parts of internal combustion engine blocks 

 

 

Features and Benefits :  

 

  • Thermal conductivity 

  • Excellent shear and peel strength 

  • Excellent adhesion 

  • Excellent adhesive properties 

  • Screen printing possible 

  • Chemically neutral  to most materials  

  • Chemically resistant to solvents, acids, alkalis 

  • High temperature resistance 

  • Has a paste structure , does not spread during polymerization 

  • Rapid polymerization of the composition when heated from 100 0 С  

  • High temperature resistance 

  • Does not require preliminary preparation and mixing, the composition is ready to use 

  • Seals the connection after curing , protects against corrosion 

  • Minimum gas permeability 

  • Minimal shrinkage during polymerization 

  • Does not contain solvents, thinners, volatile substances 

  • Long shelf life of the finished  composition , does not require special conditions  

 

Physical properties of uncured  compound 

Parameter 

Value 

Test Method or Document No.  

Chemical composition 

E poksidnaya resin 

 

Color 

Black, uniform 

 

Dynamic viscosity (at + 25 0 С) 

6 0 0  000 - 8 00  000 mPa ∙ s 

GOST 25271 

Density 

1. 55 

GOST 18995.1 - 73 

Maximum clearance between mating parts  

5  mm 

research 

 

Polymerization under standard conditions  

Temperature 

Time 

1 0 0 0 С 

120  minutes 

12 0 0 C 

40  minutes 

15 0 0 C 

20  minutes 

180 0 C 

15 minutes 

 

The actual curing time will depend on the initial temperature of the mating parts, as well as the time it takes for the adhesive and mating parts to reach the  specified temperature (depending on the size of the parts, their number, the size of the oven, its power, etc. ).  

Alternative curing methods are infrared lamps, technical hair dryers, induction heating, hot plates.  

 

Physical properties of the cured  composition 

Parameter 

Value 

Test Method or Document No.  

Shear strength  (steel) 

27 - 41  MPa  

ASTM D - 1002 

Shear strength  (aluminum) 

1 7 - 31  MPa  

ASTM D - 1002 

Shear strength  (zinc) 

14 - 27  MPa  

ASTM D - 1002 

Thermal expansion coefficient 

45 x  10 - 6 mm / ° С 

 

Hardness, Shore D 

80 

DIN 53 505 

Working temperature  

from - 40 to + 180 ° С (short - term exposure to higher temperatures is possible if the parts are not subjected to maximum load) 

research 

Thermal conductivity 

0.55 W / mK 

ASTM C177 - 10 

Dielectric strength 

17.7 kV / mm 

ASTM  D149 

Dielectric constant at 1 MHz 

~ 5 

ASTM  D150 

Dissipation factor at 1 MHz 

~ 0.02 

ASTM  D150 

 

Attention!  

If the Elastomeric Syst е ms line does  not contain the necessary RuBond series glue , then such a product can be developed especially for you (including exclusively) with the specified technical parameters.   

 

RuBond ES1 8 0 B delivering e tsya syringes under the needle mount type « Luer Lock » volume 50 ml bottles with soft spout metering  200 ml .      

According to the customer's specifications, it is possible to supply the product in a different container.  

 

Surface preparation 

The surfaces must be cleaned, dried and degreased before applying the adhesive with  any  cleaner suitable for the parts to be bonded . M Ferrous materials, having a surface oxide film, must also be machined to remove it (recommended shortly before applying the adhesive).   

 

Bonding of surfaces The adhesive should be applied through a dispenser with a suitable diameter. The composition must be applied to the entire area of the interface of the parts, since the glue does not spread during polymerization. It is enough to apply the glue to one of the surfaces, while it is necessary to avoid the formation of air bubbles in it. When the mating of the parts they need to be sufficiently strong compression to the adhesive is evenly distributed over all  glue th  surfaces wells .  
  
 
 

The parts to be joined must be compressed with each other during the entire polymerization time of the composition.  

The displacement of parts relative to each other from the moment the glue begins to reject and until the moment they are glued can lead to a deterioration in the strength characteristics of the finished unit.  

In order to avoid displacement of parts during the polymerization of the glue, it is recommended to use mechanical means of  fastening the parts, such as clamps, clamps, etc. It is recommended to keep the joint assembly stationary until the adhesive has completely hardened.  
 

 

Storage 
 

Storage temperature 

 

 

Shelf life (when stored in unopened original packaging) 
 

from + 5 to + 7 ° С 

12 months 

from + 18 to + 23  

at least 4 months 

 

When storing the composition outside the temperature range from + 5 to + 23 ° C, the manufacturer does not guarantee that the composition will retain its properties.  

 

Contact the seller
RuBond ES180 B (50ml) One-component epoxy adhesive composition, thermoset
RuBond ES180 B (50ml) One-component epoxy adhesive composition, thermoset
for
by the goods
Your message must contain at least 20 symbols. The message must not be more than 2000 symbols.
Obligatory field is not filled
The field is wrongly filled
The field is wrongly filled
Shipping method
Payment method
Compare0
ClearSelected items: 0